Longevity of composite restorations in posterior teeth placed by dental students: a 12-year retrospective study.

OBJECTIVES: To evaluate the longevity of resin composite restorations placed in posterior teeth by dental students, using data from electronic records from 2008 to 2019. MATERIALS AND METHODS: Demographic (gender and age) and clinical variables (dental group, position in dental arch, and the number of restored surfaces) were evaluated. The 5-year follow-up was assessed according to the day the restoration was placed. Kaplan-Meier curves were generated to calculate the annual failure rate. Data were analyzed by Chi-Square, Kruskal-Wallis, and Mann-Whitney tests (α = 0.05). RESULTS: In total, 3.883 records relative to return periodicity were analyzed. The final sample consisted of 900 restorations from 479 patients. The majority were females, aged between 31 and 60. In total, 256 failures were reported (success rate = 78%), showing an annual failure rate of 2.05%. The main reasons for failures were restoration replacement (55.5%), endodontics (21.9%), prosthetics (14.5%) and extraction (8.2%). There was a higher risk of failure in restorations involving three or more surfaces (p = 0.000) and in patients over 60 years (p < 0.001). In females (p = 0.030), molars (p = 0.044), and maxillary teeth (p = 0.038) failed in a shorter time. CONCLUSIONS: Resin composite restorations placed in permanent posterior teeth by dental students had high survival rates. The main reason for failure was the replacement of restorations. The age group and the number of restored surfaces significantly affected the success of the restorations. CLINICAL RELEVANCE: The electronic health records over 12 years showed that 78% of the resin restorations in posterior teeth placed by dental students were successful for a minimum of five years.

New Technique for Wedge Selection in Direct Class II Restorations: A Pilot Study.

Background: Performing an appropriate Class II direct restoration is a great challenge. The correct selection of the matrix system and the elements used for its stabilization will have a great impact on the result. The aim of this study is to show a new digital method for a predictable selection of the wedge and compare it with the conventional method. Methods: Sixty patients were randomly divided into two groups. In Group 0, the wedge was selected intraoperatively by visual examination, while in Group 1 the wedge was selected preoperatively through the measurement of the cervical embrasure on the bite-wing radiography. The number of wedges used, modifications to them, and tissue damage were registered, along with the quality of the proximal contact and the marginal adaptation. Results: Student's t-test revealed a statistical difference between the number of wedges used, which was higher in Group 0 (p < 0.05). Pearson Chi-square test showed that tissue damage was statistically higher in Group 0 (p < 0.05), while there was no statistically significant difference between groups in wedge modifications (p > 0.05). Group 1 revealed a higher frequency of satisfactory proximal contact and marginal adaptation (p < 0.05). Conclusions: This new technique reduces wedges waste and tissue damage and provides an adequate interproximal anatomy.

Assessment of Prevalence and Causative Factors for Replacement of Composite and Amalgam Restorations: An Observational Study.

Aim: This study intends to evaluate the frequency and causes of replacement for failed amalgam and composite dental restorations. Methodology: A cross-sectional study comprising female patients with failed permanent composite and amalgam restorations aged 15-60 years old was carried out at the dental clinics of Qassim University. Using a self-structured proforma, demographic data and causes for restoration failure were recorded. The effectiveness of the restorations was assessed by using the Ryge criteria after performing clinical and radiographic examinations. The Statistical Package for Social Science was used for the statistical analysis. Results: It is found that 84.6% of the 299 unsuccessful restorations examined were composite, and 15.4% were amalgam. The main reason for dental failure for both amalgam (95.6%) and composite (93.28%) restorations was secondary caries. Failure of amalgam restoration was largely caused by poor marginal adaptation. With varied incidences between amalgam and composite restorations, typical complaints included discomfort, sensitivity, pain, and food impaction with soreness. The main justification for replacement in amalgam restorations was sensitivity. Repair and replacement rates were similar for amalgam, composite, and mandibular/maxillary restorations. Moreover, 21.1% of individuals overall reported no symptoms, with 8.7% in the amalgam group and 23.3% in the composite group with significant differences (χ2 = 34.28, P = 0.001). Conclusion: According to the current study, secondary caries was found to be the main reason for both amalgam and composite restoration failure. The main problems reported were sensitivity, discomfort, and pain with amalgam showing more sensitivity-related failures.

Monowave vs. Polywave Light - Curing Units: Effect on Light Transmission of Composite without Alternative Photoinitiators.

Objective: The aim of this study was to compare the light transmission of monowave and polywave-curing devices by a bulk-fill composite containing only camphorquinone as a photoinitiator. Materials and methods: Three light-curing devices were used to cure bulk-fill composite QuiXfil: one monowave (Translux® Wave) and two polywave (VALO Cordless and Bluephase® PowerCure. The NIST-calibrated spectrometer (MARC Resin Calibrator, BlueLight Analytics Inc.) was used to measure the incident and transmitted light through a 2-mm composite specimen over 20 s. Light transmittance was calculated from the ratio of the amount of transmitted and incident light. For data analysis (ANOVA, α = 0.05), total irradiation of the entire spectrum, irradiation with wavelengths of 360-420 nm for the violet spectrum, and 420-540 nm for the blue spectrum were selected. Results: Monowave curing unit Translux® Wave had the lowest light transmission (13.78 ± 0.5%), similar to the violet light transmission of polywave devices (12.02 ± 0.94% and 13.81 ± 1.72% for Valo Cordless and Bluephase PowerCure, respectively). Blue light transmittance (32.15-23.70%) was more than twofold higher than for the wavelengths in the violet region of the spectrum (13.81-12.02%) for the two polywave devices. VALO Cordless showed the highest total and blue light transmission (p<0.001). There was no significant difference in the transmission of the violet part of the spectrum between VALO Cordless and Bluephase® PowerCure (p = 0.465). Conclusion: Within the limitations of this study, we could conclude that polywave curing devices can be used for the polymerization of the bulk-fill composite with camphorquinone as the sole photoinitiator.

Comparison of Three Different Orthodontic Adhesives Bonded to Metallic and Ceramic Brackets: SEM and SEM/EDX Analysis (In Vitro Study).

Objectives: To compare three different orthodontic adhesives (Transbond XT Light Cure Adhesive, Heliosit Orthodontic, Fuji Ortho LC) bonded to two types of orthodontic brackets: ceramic brackets (Fascination Roth 0.22) and metallic brackets (Topic Roth 0.22, Dentaurum). Materials and methods: The study was performed on 18 human teeth (6 for each adhesive). The prepared teeth were divided into three groups according to the examination time. Subsequently, they were observed after 1, 2 and 3 weeks following bonding. After the experimental procedure, the teeth samples were cut in half along the longitudinal axis in the vestibulo-oral direction, fixed with conductive carbon cement, placed in a high-vacuum evaporator and then coated with carbon. One half of each sample was observed under a Field-emission gun scanning electron microscope (FEG-SEM Hitachi SU 8030, Japan), while on the second half of the samples qualitative (X-ray line-scans) and semi-quantitative point X-ray energy dispersive analyses (EDX) were performed with Thermo Noran (USA) NSS System 7, equipped with Ultra Dry detector (30 mm2 window). Results: Transbond XT had an ideal bond with the enamel and the bracket base, with rare presence of microgaps and cracks in the enamel. Heliosit Orthodontic demonstrated a better bond relationship with the bracket base than the enamel, whereas in the latter the presence of microgaps in the bond was observed. The microphotographs of Fuji Ortho LC demonstrated many cracks inside the adhesive, and some of them continued to move forward into the enamel surface. Therefore, an impression of a very solid bond relationship with the enamel exists, with cracks being present in the enamel surface and never at the enamel-adhesive interface. Microgaps also appeared at the bracket-adhesive interface. Conclusion: Transbond XT is a highly filled composite resin and is an ideal orthodontic adhesive in each aspect examined, with an ideal enamel-adhesive and bracket-adhesive interface. Heliosit Orthodontic provides better bracket-adhesive interface compared to the enamel. Fuji Ortho LC as a solid resin-modified GIC provides a better enamel-adhesive interface, compared to the bracket base.

Development of a three-dimensional printed model from a digital impression of a real patient for aesthetic dentistry undergraduate teaching.

INTRODUCTION: The acquisition of skills and manual dexterity in aesthetic dentistry in undergraduate teaching requires preclinical practices with simulation that should approximate real clinical situations. OBJECTIVE: We will present a digital procedure for the creation of three-dimensional (3D) resin models adapted to the practices of the Aesthetic Dentistry course. MATERIAL AND METHOD: Stereolithography or Standard Tesellation Language (STL) files of a real patient were previously obtained with a 3-shape intraoral scanner. Using the Exocad computer programme for dental prosthesis design, various modifications were made, such as incisor rotation, surface alterations imitating dysplasias or erosions, the creation of diastemas, or even changes in tooth size. The virtual model was printed in resin for use by students. Once the practices were finished, the students and the teachers evaluated the use of the 3D printed models. RESULTS: The result is the typodont model, in which seven laboratory sessions took place: 1-Restoration of conoid tooth morphology, 2-Cervical abrasion/ erosion restoration, 3-Direct Composite Veneer, 4-Aesthetic correction in a tooth with rotation, 5-Diastem closure, 6-Occlusal abrasions/ erosion, and 7-Maryland bridge. 90.48% of the students evaluated the designed 3D model as the best method for laboratory practice compared to other methods, obtaining a general assessment of 8.3 out of 10. CONCLUSION: The method used has provided a reproducible standard analog model for direct aesthetic dental restoration practice, with a good assessment by students and teachers.

Biocompatibility of different resin composites after polymerization with two light curing units: an immunohistochemical study.

Purpose: The aim of this study is to compare the biocompatibility of two different resin composites after polymerization under two different light sources in three different time periods. Materials and methods: 72 polyethylene tubes polymerized with 2 different resin composites and 2 different light sources (Elipar S10 and Valo ) [Group 1: Kalore Elipar S10 (KE), Group 2: Kalore Valo (KV), Group 3: Essentia Elipar S10 (EE), Group 4: Essentia Valo (EV)] were implanted in the dorsal connective tissue of 18 rats. 24 empty polyethylene tubes [Group 5: (Control group)] were implanted in the dorsal connective tissue of 6 rats. Then, the rats were sacrificed after 7th, 15th and 30th days in each time intervals (n=8). Biopsy samples were stained with H&E and examined for inflammation, necrosis, macrophage infiltrate, giant cell and fibrous capsule criteria. Immunohistochemical staining was performed to evaluate proinflammatory cytokines (IL-1ß, IL-6 and IL-8). Results: When the composite groups and the control groups were compared; the difference was statistically significant for the criteria of inflammation at 7th and 15th days, there was no statistical difference between the time points in terms of fibrous capsule and necrosis. When the composite groups and control groups were evaluated in terms of proinflammatory cytokines; statistically significant differences were found at 7th, 15th and 30th days. Conclusion: All CRs used in this study showed acceptable biocompatibility in the subcutaneous tissues of rats after polymerization with different light sources.

Effect of polishing versus glazing of CAD-CAM ceramics on wear and surface roughness of opposing composite resin.

Background: This study aimed to assess the effect of polishing versus glazing of computer-aided design-computer-aided manufacturing (CAD-CAM) ceramics on depth of wear and surface roughness of opposing composite resin. Materials and Methods: This in vitro study was conducted on 40 Z250 composite and 40 CAD-CAM ceramic specimens including Celtra Duo, Vita Mark II, e.max CAD, and Vita Suprinity ceramics. All ceramic specimens were roughened by a fine-grit bur after primary glazing to simulate an adjusted surface in the clinical setting. They were then randomly assigned to two subgroups and underwent reglazing or polishing. All composite and ceramic specimens underwent profilometry after surface treatment and prior to the wear test, and the results were recorded quantitatively. Composite specimens were then subjected to 120,000 wear cycles against ceramic specimens in a chewing simulator, and the depth of wear was measured by a scanner. Data were statistically analyzed by repeated measures two-way analysis of variance (ANOVA) and one-way ANOVA (α = 0.05). Results: Comparison of the surface roughness of composite specimens before and after the wear test revealed significant differences in both glazed Suprinity (P = 0.048) and Vita Mark II (P = 0.026) ceramics groups. The change in surface roughness after the wear test (compared with baseline) was significant in glazed (P = 0.000) and polished (P = 0.013) Vita Mark II and polished Suprinity (P = 0.037) ceramics, but this change was not significant in other ceramics (P > 0.05). The depth of wear after the wear test was not significantly different among the ceramic and composite subgroups (P > 0.05). Conclusion: Assessment of depth of wear and surface roughness of composite specimens showed that the polishing kits of CAD-CAM ceramics can serve as a suitable alternative to reglazing.

Comparison of coronal sealing of flowable composite, resin-modified glass ionomer, and mineral trioxide aggregate in endodontically treated teeth: An in-vitro study.

Background: Coronal seal is one of the essential factors that affects the success of endodontic treatment and reinforces the apical seal. The intra-orifice barrier is an efficient alternative approach to decrease coronal leakage in endodontically treated teeth and various materials have been used for this purpose. This study aimed to compare the coronal sealing of flowable composite, resin-modified glass ionomer (RMGI), and mineral trioxide aggregate (MTA) in endodontically treated teeth. Materials and Methods: In this in vitro study, 35 single-canal canine teeth were divided into five groups, including flowable composite, RMGI, MTA, positive control, and negative control groups. The teeth were filled with restorative materials according to the factory's instructions. Afterward, the samples were immersed in 2% methylene blue dye solution for 1 week at 37°C and 100% humidity condition. Finally, the teeth were sectioned longitudinally and dye penetration was measured using a stereomicroscope with ×10. Data were analyzed with Kolmogorov-Smirnov and Kruskal-Wallis tests (α = 0.05). Results: The positive control group showed the highest amount of dye penetration compared to other groups (12.34 ± 0.46). Dye penetration in the MTA group was significantly lower (4.25 ± 0.31) compared to the RMGI group (5.94 ± 0.24) (P = 0.02). Moreover, while the dye penetration in the MTA group was lower than in the flowable composite group (5.65 ± 0.26), the difference was not statistically significant (P = 0.12). Conclusion: MTA reduces the coronal leakage and provides an acceptable coronal seal in endodontically treated teeth, especially compared to RMGI, and therefore, using MTA as an intra-orifice barrier increases the endodontic treatment success rate.

Fracture resistance of CAD/CAM endocrowns made from different materials in maxillary premolar interproximal defects.

OBJECTIVES: This in vitro study aims to compare the fracture resistance of three CAD/CAM materials used in endocrown restoration of interproximal defects in maxillary premolars. MATERIALS AND METHODS: 45 maxillary premolars extracted as part of orthodontic treatment were included. Following standardized root canal treatment, all teeth were prepared into Mesial-Occlusal (MO) cavity types. The samples were then randomly divided into three groups: LD [repaired with lithium disilicate glass ceramics (IPS e.max CAD)], VE [treated with polymer-infiltrated ceramics (Vita Enamic)], and LU [repaired with resin-based nanoceramics (Lava Ultimate)]. Axial static loading was applied using a universal testing machine at 1 mm/min until fracture, and fracture resistance and failure modes were recorded. RESULTS: Regarding Fracture Resistance Values (FRVs), the LD group exhibited significantly higher values than the other two groups, VE (P = 0.028) and LU (P = 0.005), which showed no significant difference (P = 0.778). On the other hand, regarding failure modes, the LD group had a higher prevalence of irreparable fractures compared to the other two groups, VE (P < 0.001) and LU (P < 0.001), which showed no significant difference. CONCLUSIONS: Although lithium disilicate glass ceramics exhibited higher FRVs, they had a lower repair probability. In contrast, polymer-infiltrated ceramics and resin-based nanoceramics contributed to tooth structure preservation. CLINICAL RELEVANCE: For maxillary premolars with interproximal defects following root canal treatment, resin ceramic composites are recommended for restoration to enhance abutment teeth protection.

Adhesion and sealing of different universal adhesive systems associated with bulk-fill resins after using endodontic irrigation solutions: An in vitro study.

This study aimed to evaluate the interface of universal adhesive (UA) with bulk-fill resin (BF) and dentin, after endodontic irrigation. The pulp chamber of 96 molars was irrigated with chlorhexidine 2% (CHX) or sodium hypochlorite 5.25% (NaOCl) and restored according to three restorative protocols. Microtensile bond strength (µTBS) and nanoleakage tests were performed after 24 h of thermocycling. Kruskal Wallis, Mann-Whitney and Wilcoxon were performed (p < 0.05). Comparing restorative systems, a difference was found only when irrigated with CHX after 24 h. CHX provided higher µTBS than NaOCl after 24 h for two restorative protocols; after thermocycling, NaOCl provided the greatest µTBS than CHX for one group. Decreased µTBS was observed for all restorative systems when CHX was used after thermocycling. NaOCl demonstrated the highest nanoleakage. The composition of UA influenced the immediate adhesion and sealing to BF when CHX was used; ageing has a deteriorating effect on adhesion and sealing for all restorative systems.

A Randomised Controlled Trial of Postoperative Sensitivity after Class II Restoration with Bulk-Fill vs Conventional Composites.

AIM: Insufficient evidence is available in quantifying the retention between the simplified and conventional non-balanced dentures. The aim of the study was to quantify, compare the maxillary denture retention and patient satisfaction between conventional and simplified removable non-balanced complete dentures. METHOD: The randomized clinical trial recruited 44 patients (n=22) with definitive criteria. Simplified and conventional non-balanced complete dentures were fabricated for the intervention groups. The denture retention of maxillary complete denture was assessed with dynamometer and patient satisfaction with visual analogue scale. The mean retention of maxillary denture and satisfaction were recorded at 0-,3-, and 6 - month interval. The data were statistically analyzed. (α=.05). RESULTS: The mean ±SD of retention for conventional denture at 0, 3, and 6 months by dynamometer ranged from 121.73 ± 1.64 N to 120.55 ± 1.57 N and 110.77 ±1.45N to 109.59±1.97 N for simplified denture. The mean ±SD of visual analogue score varied between 9.45±0.35 to 7.19± 0.69 for conventional dentures and 8.00 ±1.39 to 6.81±0.82 for simplified dentures. The repeated ANOVA, t-test and post-hoc Bonferroni revealed statistically significant differences between the two types of denture. (P⟨.05) Conclusion: Numerical retention and satisfaction were higher in conventional non-balanced denture than simplified denture.

Bonding performance and interfacial adaptation of modern bulk-fill restorative composites after aging in artificial saliva: an in vitro study.

OBJECTIVES: This study aimed at comparing the microtensile bond strength (MTBS) and interfacial adaptation of a modern self-curing and a light-curing restorative bulk-fill composite to a conventional composite applied with the layering technique. METHODS: Forty-eight occlusal cavities were divided in three main groups (16/group) based on tested materials: (i) STELA, bulk-fill self-curing restorative (STELA, SDI Ltd.); (ii) 3 M-BULK, bulk-fill composite (Filtek One Bulk-Fill, 3 M Oral Care); and (iii) 3 M-CTR, a conventional composite (Filtek Supreme XTE, 3 M Oral Care). These were used in combination with their adhesives in self-etch (SE) or etch-and-rinse (ER) mode. Specimens stored in artificial saliva (24 h or 12 months) were evaluated for MTBS and fractography. The interfacial analysis was performed through confocal microscopy. ANOVA and Fisher's LSD post hoc tests were performed with a level of significance of 5%. RESULTS: All the tested materials applied in ER mode presented (24 h) greater bond strength than in SE mode. Although all materials showed a significant drop in the bond strength after prolonged storage, STELA showed the highest bonding performance and interfaces with few gaps. 3 M-BULK had the lowest bond strength and an interface with several voids and gaps. CONCLUSIONS: All materials were affected by interface degradation and bonding reduction over prolonged aging. However, their use in combination with adhesives applied in ER mode may offer greater immediate bonding performance. CLINICAL RELEVANCE: The use of restorative light-curing bulk-fill composites may generate gaps at the bonding interface and voids. STELA may represent a suitable alternative to avoid such issues.

In-vitro-cytotoxicity of self-adhesive dental restorative materials.

OBJECTIVES: Although the introduction of self-adhesive composites in restorative dentistry is very promising, the innovation of new materials also presents challenges and unknowns. Therefore, the aim of this study was to investigate the cytotoxicity of four different self-adhesive composites (SAC) in vitro and to compare them with resin-modified glass ionomer cements (RM-GIC), a more established group of materials. METHODS: Samples of the following materials were prepared according to ISO 7405/10993-12 and eluted in cell culture medium for 24 h at 37 °C: Vertise Flow, Fusio Liquid Dentin, Constic, Surefil One, Photac Fil and Fuji II LC. Primary human pulp cells were obtained from extracted wisdom teeth and cultured for 24 h with the extracts in serial dilutions. Cell viability was evaluated by MTT assay, membrane disruption was quantified by LDH assay and apoptosis was assessed by flow cytometry after annexin/PI staining. RESULTS: Two SAC (Constic and Vertise Flow) and one RM-GIC (Photac Fil) significantly reduced cell viability by more than 30% compared to the untreated control (p < 0.001). Disruptive cell morphological changes were observed and the cells showed signs of late apoptosis and necrosis in flow cytometry. Membrane disruption was not observed with any of the investigated materials. CONCLUSION: Toxic effects occurred independently of the substance group and need to be considered in the development of materials with regard to clinical implications. CLINICAL SIGNIFICANCE: SAC have many beneficial qualities, however, the cytotoxic effects of certain products should be considered when applied in close proximity to the dental pulp, as is often required.

Degradation effects of dietary solvents on microhardness and inorganic elements of computer-aided design/computer-aided manufacturing dental composites.

BACKGROUND: Computer-aided design/computer-aided manufacturing (CAD/CAM) dental composites were introduced with superior mechanical properties than conventional dental composites. However, little is known on effects of dietary solvents on microhardness or inorganic elemental composition of CAD/CAM composites. OBJECTIVES: The objectives of this study were to evaluate the degradation effects of each dietary solvent on the microhardness of the different CAD/CAM dental composites and to observe the degradation effects of dietary solvent on the inorganic elements of the dental composites investigated. METHODS: Fifty specimens with dimensions 12 mm x 14 mm x 1.5 mm were prepared for direct composite (Filtek Z350 XT [FZ]), indirect composite (Shofu Ceramage [CM]), and three CAD/CAM composites (Lava Ultimate [LU], Cerasmart [CS], and Vita Enamic [VE]). The specimens were randomly divided into 5 groups (n = 10) and conditioned for 1-week at 37°C in the following: air (control), distilled water, 0.02 N citric acid, 0.02 N lactic acid and 50% ethanol-water solution. Subsequently, the specimens were subjected to microhardness test (KHN) using Knoop hardness indenter. Air (control) and representative postconditioning specimens with the lowest mean KHN value for each material were analyzed using energy dispersive X-ray spectroscopy (EDX). Statistical analysis was done using one-way ANOVA and post hoc Bonferroni test at a significance level of p = 0.05. RESULTS: Mean KHN values ranged from 39.7 ± 2.7 kg/mm2 for FZ conditioned in 50% ethanol-water solution to 79.2 ± 3.4 kg/mm2 for VE conditioned in air (control). With exception to LU, significant differences were observed between materials and dietary solvents for other dental composites investigated. EDX showed stable peaks of the inorganic elements between air (control) and representative postconditioning specimens. CONCLUSIONS: The microhardness of dental composites was significantly affected by dietary solvents, except for one CAD/CAM composite [LU]. However, no changes were observed in the inorganic elemental composition of dental composites between air (control) and 1-week postconditioning.

Repair bond strength of a new self-adhesive composite resin to three different resin-matrix ceramic CAD-CAM materials.

This study aimed to evaluate the shear bond strength of two flowable composite resins to resin-matrix ceramic CAD-CAM materials.Fifty-four plates obtained from Lava Ultimate (LU), Cerasmart (CS), and Vita Enamic (VE) CAD-CAM blocks were assigned to nine groups: N0: Nova Compo SF (NCSF), N1: Silane/Single Bond Universal (SBU)/NCSF, N2: SBU/NCSF, N3: Silane/G-Premio Bond (GPB)/NCSF, N4: GPB/NCSF, G1: Silane/SBU/G-aenial Universal Injectable Composite (GUIC), G2: SBU/GUIC, G3: Silane/GPB/GUIC, G4: GPB/GUIC. After the repair procedures, shear bond strength values were analyzed. Silane pre-application decreased bond strength in most LU and CS groups but increased it in VE. NCSF performed better than GUIC in all CAD-CAM's with similar adhesive protocols. SBU in combination with NSCF had the highest bond strength among all repair procedures in LU and CS. Silane-containing universal adhesives in combination with self-adhesive resin composites should be used to repair resin-matrix ceramic materials.

In silico nonlinear dynamic finite-element analysis for biaxial flexural strength testing of CAD/CAM materials.

PURPOSE: The aim of this study was to establish and assess the validity of in silico models of biaxial flexural strength (BFS) tests to reflect in vitro physical properties obtained from two commercially available computer-aided design/computer-aided manufacturing (CAD/CAM) ceramic blocks and one CAD/CAM resin composite block. METHODS: In vitro three-point bending and BFS tests were conducted for three CAD/CAM materials (n = 10): Katana Zirconia ST10 (raw material: super-translucent multilayered zirconia, ST10; Kuraray Noritake Dental, Niigata, Japan), Katana Zirconia HT10 (raw material: highly translucent multilayered zirconia, HT10; Kuraray Noritake Dental), and Katana Avencia N (AN; Kuraray Noritake Dental). Densities, flexural moduli, and fracture strains were obtained from the in vitro three-point bending test and used as an input for an in silico nonlinear finite element analysis. The maximum principal stress (MPS) distribution was obtained from an in silico BFS analysis. RESULTS: The elastic moduli of AN, HT10, and ST10 were 6.513, 40.039, and 32.600 GPa, respectively. The in silico fracture pattern of ST10 observed after the in silico evaluation was similar to the fracture pattern observed after the in vitro testing. The MPS was registered in the center of the tensile surface for all three specimens. The projections of the supporting balls were in the form of a triple asymmetry. CONCLUSIONS: The in silico approach established in this study provided an acceptable reflection of in vitro physical properties, and will be useful to assess biaxial flexural properties of CAD/CAM materials without wastage of materials.

Mechanical properties of 3D-printed and milled composite resins for definitive restorations: An in vitro comparison of initial strength and fatigue behavior.

OBJECTIVE: To evaluate the flexural strength and fatigue behavior of a novel 3D-printed composite resin for definitive restorations. MATERIALS AND METHODS: Fifty disc-shaped specimens were manufactured from each of a nanohybrid composite resin (NHC), polymer-infiltrated ceramic network (PICN), and 3D-printed composite resin (3D) with CAD-CAM technology. Biaxial flexural strength (σin ) (n = 30 per group) and biaxial flexural fatigue strength (σff ) (n = 20 per group) were measured using piston-on-three-balls method, employing a staircase approach of 105 cycles. Weibull statistics, relative-strength degradation calculations, and fractography were performed. The results were analyzed with 1-way ANOVA and Games-Howell post hoc test (α = 0.05). RESULTS: Significant differences in σin and σff among the groups (p < 0.001) were detected. The NHC group provided the highest mean ± standard deviation σin and σff (237.3 ± 31.6 MPa and 141.3 ± 3.8 MPa), followed by the PICN (140.3 ± 12.9 MPa and 73.5 ± 9.9 MPa) and the 3D (83.6 ± 18.5 MPa and 37.4 ± 23.8 MPa) groups. The 3D group exhibited significantly lower Weibull modulus (m = 4.7) and up to 15% higher relative strength degradation with areas of nonhomogeneous microstructure as possible fracture origins. CONCLUSIONS: The 3D-printed composite resin exhibited the lowest mechanical properties, where areas of nonhomogeneous microstructure developed during the mixing procedure served as potential fracture origins. CLINICAL SIGNIFICANCE: The clinical indications of the investigated novel 3D-printed composite resin should be limited to long-term provisional restorations. A cautious procedure for mixing the components is crucial before the 3D-printing process, since nonhomogeneous areas developed during the mixing could act as fracture origins.

Analysis of color stability and degree of conversion of different types of resin composites

Abstract Resin composites containing surface pre-reacted glass (S-PRG) have been introduced to reduce demineralization and improve remineralization of the tooth structure. However, water diffusion within the material is necessary for its action, which can impair its overall physicomechanical properties over time, including color stability. This study aimed to evaluate the color stability and related degree of conversion (DC) of four resin composites. Discs (6 x 4 mm, n = 5/group) of microhybrid (MH), nanofilled (NF), nanohybrid (NH), and S-PRG-based nanohybrid (S-PRG-NH) composites with two opacities (A2/A2E and A2O/A2D) were prepared. Color (CIELab and CIEDE2000) was evaluated with a spectrophotometer after aging in grape juice (2 x 10 min/10mL/7days). The DC was analyzed by using Fourier transform infrared spectroscopy before and after light-curing. Data were statistically analyzed by using two-way analysis of variance and post-hoc least significant difference tests (p<0.05). In the color stability analysis, the interaction between filler type and opacity was significant (CIELab, p = 0.0015; CIEDE2000, p = 0.0026). NH presented the highest color stability, which did not differ from that of MH. The greatest color alteration was observed for S-PRG-NH. S-PRG fillers also influenced DC (p < 0.05). The nanohybrid resin composite presented favorable overall performance, which is likely related to its more stable organic content. Notwithstanding the benefits of using S-PRG-based nanohybrid resins, mostly in aesthetic procedures, professionals should consider the susceptibility of such resins to color alteration, probably due to the water-based bioactive mechanism of action.

In vitro characterization of a novel resin-based restorative material containing alkaline fillers

Abstract Objective: In this study, a comparative evaluation of the physicochemical properties of Cention N and other direct restorative materials was performed. Three restorative materials—a resin-modified glass ionomer (Fuji II LC), an alkasite-based resinous material (Cention N), and a resin composite (Tetric N Ceram)—were characterized in terms of degree of conversion, Knoop hardness number (KHN) ratio, flexural strength, elastic modulus, water sorption, water solubility, microshear bond strength to dentin, immediate microleakage, and radiopacity. Methodology: The microshear bond strength to dentin and microleakage of Cention N were evaluated with and without the application of an adhesive system (Tetric N Bond Universal). A one-way ANOVA test was used to analyze the data in terms of degree of conversion, KHN ratio, water sorption, water solubility, microshear bond strength to dentin, and radiopacity. A two-way ANOVA test (carried out considering the material type and ethanol aging as factors) was used to analyze the data in terms of flexural strength and elastic modulus. The Kruskal-Wallis test was used to statistically analyze the data on microleakage. A significance level of α=0.05 was used for all tests. Results: Fuji II LC was found to have the highest degree of conversion, water sorption, and microleakage, as well as the lowest flexural strength. Cention N had the highest solubility; when used with an adhesive system, it achieved bond strength and microleakage similar to those of the Tetric N Ceram composite. Tetric N Ceram had the highest degree of conversion, KHN ratio, and radiopacity. Conclusion: The properties of Cention N validate its efficacy as an alternative direct restorative material when used in conjunction with an adhesive system.